基于拉曼光谱实时检测的碳化钢筋混凝土再碱化机理探究
Mechanism Investigations of Realkalization for Carbonated Reinforced Concrete Based on Real Time Raman Spectroscopy Analysis
投稿时间:2016-11-16  修订日期:2017-05-02
DOI:103969/j.issn.1007 9629201706011
中文关键词:  电化学再碱化处理  碳化钢筋混凝土  腐蚀产物  拉曼光谱  腐蚀电位  腐蚀电流密度
英文关键词:electrochemical realkalization treatment  carbonated reinforced concrete  corrosion product  Raman spectroscopy  corrosion potential  corrosion current density
基金项目:国家自然科学基金青年基金资助项目(51408546);浙江省自然科学基金青年基金资助项目(LQ14E080008);浙江省文物保护科技项目(2015018);浙江省科技厅公益项目(2015C33058)
        
作者单位
童芸芸
TONG Yunyun
浙江科技学院土木与建筑工程学院,浙江杭州310023
School of Civil Engineering and Architecture, Zhejiang University of Science & Technology, Hangzhou 310023, China
叶良
YE Liang
浙江科技学院土木与建筑工程学院,浙江杭州310023
School of Civil Engineering and Architecture, Zhejiang University of Science & Technology, Hangzhou 310023, China
马超
MA Chao
浙江科技学院土木与建筑工程学院,浙江杭州310023
School of Civil Engineering and Architecture, Zhejiang University of Science & Technology, Hangzhou 310023, China
摘要点击次数: 195
全文下载次数: 
中文摘要:
      为了从本质上解释再碱化技术对碳化钢筋混凝土的修复机理,通过1个隔绝外界空气和电解质溶液的模拟混凝土/钢筋界面,利用拉曼光谱技术实现了对碳化钢筋混凝土再碱化修复过程中腐蚀产物成分变化的实时检测.结果表明:经过强加电流式人工加速腐蚀钢筋后,腐蚀产物主要成分为绿锈.在再碱化修复过程中,2个反应同时发生:绿锈被还原为氢氧化亚铁(Fe(OH)2),并转变为四氧化三铁(Fe3O4).酚酞显色试验结果和Fe3O4的生成证明了再碱化技术能够有效提高混凝土的碱性.电化学检测结果进一步证明了再碱化技术可以有效减小钢筋的腐蚀概率,降低钢筋的腐蚀活性并使之达到中等程度,但是并没有使钢筋再钝化.
英文摘要:
      In order to fundamentally explain the repair mechanisms of realkalization technology for carbonated reinforced concrete, a real time Raman study was undertaken, on a simulated concrete/steel rebar interface without direct contact with the air and the electrolyte solution, to observe the evolution of corrosion products during realkalization treatment. The results indicate that the main corrosion product is green rust after artificial corrosion acceleration by impressed current. During the realkalization treatment, two reactions occur simultaneously, green rust is reduced into brucite(Fe(OH)2) and converted into magnetite(Fe3O4). The phenolphalein tests and the production of magnetite show that the realkalization technology can effectively increase the concrete alkalinity. The electrochemical measurements further indicate that the realkalization technology can effectively decrease the corrosion probability and corrosion activity of steel rebar to medium level, however, the steel rebars can not be repassivated.