氯氧镁钢筋混凝土中涂层钢筋腐蚀的电化学特性
Electrochemical Characteristics of Coated Steel Bars Corrosion of Magnesium Oxychloride Reinforced Concrete
投稿时间:2019-06-10  修订日期:2019-06-17
DOI:103969/j.issn.1007 9629201906024
中文关键词:  氯氧镁钢筋混凝土  涂层钢筋  开路电位  腐蚀电流密度  极化电阻
英文关键词:magnesium oxychloride reinforced concrete  coated steel bar  corrosion open circuit potential  corrosion current density  polarization resistance
基金项目:国家自然科学基金资助项目(51468039,51868044)
              
作者单位
乔宏霞
QIAO Hongxia
兰州理工大学甘肃省土木工程防灾减灾重点实验室,甘肃兰州730050
Key Laboratory of Civil Engineering Disaster Prevention and Mitigation of Gansu Province, Lanzhou University of Technology, Lanzhou 730050, China
温少勇
WEN Shaoyong
兰州理工大学甘肃省土木工程防灾减灾重点实验室,甘肃兰州730050
Key Laboratory of Civil Engineering Disaster Prevention and Mitigation of Gansu Province, Lanzhou University of Technology, Lanzhou 730050, China
王鹏辉
WANG Penghui
兰州理工大学甘肃省土木工程防灾减灾重点实验室,甘肃兰州730050
Key Laboratory of Civil Engineering Disaster Prevention and Mitigation of Gansu Province, Lanzhou University of Technology, Lanzhou 730050, China
杨振清
YANG Zhenqing
兰州理工大学甘肃省土木工程防灾减灾重点实验室,甘肃兰州730050
Key Laboratory of Civil Engineering Disaster Prevention and Mitigation of Gansu Province, Lanzhou University of Technology, Lanzhou 730050, China
杨天霞
YANG Tianxia
兰州理工大学甘肃省土木工程防灾减灾重点实验室,甘肃兰州730050
Key Laboratory of Civil Engineering Disaster Prevention and Mitigation of Gansu Province, Lanzhou University of Technology, Lanzhou 730050, China
摘要点击次数: 119
全文下载次数: 0
中文摘要:
      通过Z350电化学工作站,研究了氯氧镁钢筋混凝土中裸露钢筋和涂层钢筋在不同环境中的开路电位、极化电阻及腐蚀电流密度,并且利用扫描电镜(SEM)和X射线衍射(XRD)对腐蚀产物进行分析.结果表明:锌美特(XMT)涂层在不同环境中可以很好地保护钢筋免受腐蚀,氯氧镁钢筋混凝土中涂层钢筋在水、氯盐溶液和硫酸盐溶液中的腐蚀电流密度是裸露钢筋的1/35,1/43和1/19;氯氧镁钢筋混凝土中裸露钢筋表面存在疏松多孔的层状和块状腐蚀产物,而涂层钢筋表面只存在点蚀.由此可见,XMT涂层对氯氧镁混凝土中的钢筋有一定的防腐效果.
英文摘要:
      The open circuit potential, polarization resistance and corrosion current density of bare steel bars and coated steel bars of magnesium oxychloride reinforced concrete in different environments were studied by Z350 electrochemical workstation, and the corrosion products were analysed by scanning electron microscopy(SEM) and X ray diffraction(XRD). The results show that Zinc(XMT) coating can protect steel bars from corrosion in different environments. The corrosion current density of coated steel bars in water, chloride solution and sulfate solution in magnesium oxychloride reinforced concrete is only 1/35,1/43 and 1/19 of that of bare steel bars. There are loose porous layered and massive corrosion products on the exposed steel bars surface of the magnesium oxychloride reinforced concrete, while only pitting corrosion exists on the surface of the coated steel bars. It can be seen that the XMT coating has a certain anti corrosion effect on the steel bars in the magnesium oxychloride reinforced concrete.